Retentiveness of metal coping luted to teeth of uremic patients undergoing hemodialysis using five different luting cements.

OBJECTIVES: This study aimed to assess the retention of metal copings luted to uremic teeth with five different luting agents. METHODS: A total of 35 sound natural molars was collected from uremic patients and randomly assigned into five groups (n=7). The teeth were prepared for metal copings using diamond tips and water coolant. Metal copings with a loop on the occlusal surface were fabricated using base metal alloy (Rexillium III). The copings were luted using Fuji I, glass ionomer (GI); Fuji Plus, resin-modified glass ionomer (RMGI); Panavia F 2.0, resin cement; Rely X Unicem, self-adhesive cement (SA); and Adhesor, zinc phosphate cement (ZPh). All specimens were incubated at 37 degrees C for 24 hours, conditioned in artificial saliva for 7 days, and then thermocycled for 5000 cycles (5 degrees C-55 degrees C). The dislodging force was measured using a universal testing machine at a crosshead speed of 2 mm/min. The mode of failure of the loaded adhesive copings was evaluated. Statistical analyses were performed using one-way analysis of variance and Tukey post hoc test. RESULTS: GI and SA cements had the highest and the lowest mean retentive strength, respectively (580.90+/-17.3, 406.6+/-12.7). There was no significant difference between ZPh, SA, and resin cements. These cements were inferior to GI and RMGI cements (p<0.05), which showed statistically similar retentive strengths. CONCLUSIONS: The results of this study support the use of glass ionomer and resin-modified glass ionomer cements for luting of metal copings to uremic teeth with retentive preparations.