Adhesive luting of new CAD/CAM materials.

OBJECTIVE: To evaluate the adhesive bonding performance of recently introduced tooth-colored CAD/CAM materials after different pretreatment protocols and using different luting materials. MATERIALS AND METHODS: The CAD/CAM materials under investigation were e.max CAD (lithium disilicate glass ceramic; Ivoclar Vivadent, Schaan, Liechtenstein), Celtra Duo (zirconia-reinforced lithium disilicate ceramic; Dentsply DeTrey, Konstanz, Germany), Lava Ultimate (resin nano ceramic; 3M ESPE, Neuss, Germany), and Enamic (resin infiltrated ceramic; Vita, Bad Sackingen, Germany). A total of 240 blocks (n = 5) received various pretreatments (no pretreatment, silane, sandblasting, sandblasting + silane, hydrofluoric acid, hydrofluoric acid + silane), and then different classes of adhesive luting composites were applied (adhesive: Prime&Bond XP + SCA + Calibra; Dentsply DeTrey; self adhesive: RelyX Unicem; 3M ESPE). After 24 h water storage and 10,000 thermocycles (5 degrees C/55 degrees C), specimens were cut into beams and microtensile bond strengths were recorded. RESULTS: Bonding performance of recent CAD/CAM materials was clearly influenced by the pretreatment method (P < 0.05). In general, significantly higher mu-TBS values were recorded for the ceramic materials compared to the hybrid materials (P < 0.05). Among the hybrid materials, Enamic exhibited higher bond strengths than Lava Ultimate (P < 0.05). However, despite the differences found, all materials showed a high level of bonding performance, being sufficient to withstand intraoral chewing forces during mastication. CONCLUSION: When pretreated as recommended by the manufacturers, recent tooth-colored CAD/CAM materials show an encouraging bonding performance for adhesive luting.