Shear bond strength and debonding characteristics of a new premixed self-etching with a reference total-etch adhesive.

BACKGROUND: To determine the shear bond strength and adhesive remnant index of a new premixed self-etching primer and adhesive (Tectosan, BonaDent, Germany) for orthodontic appliances in comparison to a reference total-etch system Transbond XT. METHODS: Bovine incisors were embedded in resin and randomly divided into two groups of 16 samples each. Brackets (Discovery, Dentaurum, Germany) were bonded in group 1 (total-etch-system, Transbond XT) and in group 2 (self-etch-system, Tectosan) with curing light for 40 s. Shear bonding strengths were measured after 24 h of storage in distilled water at 37 degrees C with a Zwicki 1120 testing machine (Zwick Roell, Germany). A force was applied on the bracket base at the wings in occluso-gingival direction. Then the adhesive remnant index (ARI) was determined. RESULTS: No statistical differences on SBS were found for both bonding agents (p = 0.63). ARI scores however differed statistically significantly (p = 0.035): in the total-etch group more adhesive remained on the teeth, whereas in the self-etch group more adhesive remained on the brackets. There were no visible enamel damages in both groups. CONCLUSIONS: No differences in the shear bond strength were found between both bonding agents. In our study the self-etch-system shifted the adhesive remnant index from more adhesive on the teeth to more adhesive on the bracket - as other already published self-etch systems did - with the new benefit of not increased enamel damages. Tectosan might therefore be a promising alternative to adhesive systems.