Evaluation of the biological behaviour of various dental implant abutment materials on attachment and viability of human gingival fibroblasts.

OBJECTIVE: This study aimed to investigate the biological effects of yttria-stabilized zirconia (Y-TZP) compared to other dental implant abutment materials, i.e. lithium disilicate (LS2) and titanium alloy (Ti), as well as the effects of aging of Y-TZP on viability/proliferation and attachment properties of Human Gingival Fibroblasts (HGFs). METHODS: Cylindrical specimens of each material were prepared as per manufacturer's instructions. Y-TZP specimens were divided into three groups: 1. no aging (Zr0), 2. aging for 5 h, 134 degrees C, 2 bars, 100% humidity (Zr5), 3. aging for 10 h under the same conditions (Zr10). Surface roughness was evaluated by optical profilometry; cell metabolic activity/viability by MTT assay, morphological changes by Scanning Electron Microscopy (SEM) and ratio of live/dead cells by confocal microscopy. RESULTS: Results showed statistically significant reduction of HGF metabolic activity/viability in contact with Y-TZP after aging. Nevertheless, non-aged zirconia showed no significant differences compared with LS2, Ti and control cultures. In contrast, significant stimulation of cell metabolic activity/viability was observed in HGFs exposed to LS2 eluates. Differential morphological patterns were observed for HGF in contact with different materials/treatments, with obviously increased number of dead cells and sparser distribution of HGFs cultured on Zr10 specimens. These effects were not correlated with surface topography, since Y-TZP aging did not alter surface micro-roughness. SIGNIFICANCE: These findings indicate that Y-TZP shows comparable biological properties to Ti and LS2 as implant abutment material. Nevertheless, Y-TZP aging might influence gingival cell attachment and proliferation properties, providing an alert to a potentially negative effect on the long-term maintenance of gingival architecture.