[All-ceramic premolar guiding plate retains resin-bonded fixed partial dentures].

OBJECTIVE: This study aims to investigate the fracture resistance and short-term restorative effects of resin-bonded fixed partial dentures (RBFPDs) made from heat-pressed lithium-disilicate-based glass-ceramic (IPS e.max press) and zirconia ceramic (WIELAND) and retained by all-ceramic guiding plates when used to restore missing mandibular second premolars. METHODS: A total of 64 human mandibular first premolars and first molars were prepared as abutments, then were randomly divided into 4 groups (n=8): E0, heat-pressed ceramic RBFPDs, no cyclic loading; E1, heat-pressed ceramic RBFPDs exposed to 300 000 cycles of dynamic loading; W0, zirconia ceramic RBFPDs, no cyclic loading; and W1, zirconia ceramic RBFPDs exposed to 300 000 cycles of dynamic loading. Fracture strength was tested in a universal testing machine. RESULTS: The medians of fracture strength were 1 242.85 N+/-260.11 N (E0), 1 650.85 N+/-206.77 N (W0), 1 062.60 N+/-179.98 N (E1), and 1 167.61 N+/-265.50 N (W1). Statistical analysis showed that all the groups exhibited significantly higher fracture strength compared with the maximum bite force in the premolar region (360 N; P<0.001). The W0 group had significantly higher fracture strength than the E0 group (P<0.05). Meanwhile, no significant difference in fracture strength was observed between the E1 and W1 groups (P>0.05). Significant statistical differences were found between the zirconia ceramic groups (W0 and W1, P<0.05) but not between the glassceramic groups (E0 and E1, P>0.05) after dynamic loading. CONCLUSIONS: The RBFPDs retained by all-ceramic guiding plates exhibited promising fracture properties and optimal short-term restorative effects when used to restore missing mandibular second premolars.