The objective of this study was to compare potassium hydrogen difluoride (KHF(2)) etching for zirconia with commonly used surface roughening and chemical bonding methods (silane, MDP-monomer primer) for resin-based luting cement bonding to zirconia. Zirconia specimens were divided into six groups (n=10) according to surface treatment and bonding procedures, with and without thermocycling (6,000 cycles, 5-55 masculineC): 1) air-borne particle abrasion with alumina+MDP-monomer (ABP), 2) air-borne particle abrasion with silica-coated trialuminium trioxide+silane (ABPR-S) and 3) KHF(2) etching+silane (ETC). Surface roughness and bond strength (SBS-test) for dry and thermocycled specimens were measured. SBS did not vary statistically between the dry groups, but thermocycling decreased the bond strengths of all the tested methods (p<0.05). After thermocycling, ABP had statistically significantly lower bond strength values compared to ABPR-S and ETC (p<0.05). Etching method with KHF(2) did not provide better bonding capacity to previously introduced and commonly adopted bonding methods.
No clinical trial protocols linked to this paper
Clinical trials are automatically linked when NCT numbers are found in the paper's title or abstract.PICO Elements
No PICO elements extracted yet. Click "Extract PICO" to analyze this paper.
Paper Details
MeSH Terms
Associated Data
No associated datasets or code repositories found for this paper.
Related Papers
Related paper suggestions will be available in future updates.