Influence of the resin-coating technique on the bonding performance of self-adhesive resin cements in single-visit computer-aided design/computer-aided manufacturing resin restorations.

OBJECTIVE: This in vitro study investigated the influence of resin coating on the bonding performance of self-adhesive resin cements in single-visit computer-aided design (CAD)/computer-aided manufacturing (CAM) resin restorations. MATERIALS AND METHOD: CAD/CAM resin (1.5-mm thick) was mounted on 20 noncoated and 20 resin-coated human dentin surfaces using dual-cured self-adhesive resin cements (Panavia SA Cement Plus or Panavia SA Cement Universal, Kuraray Noritake Dental) in either self-curing or dual-curing mode. These specimens were sectioned into beam-shaped sticks and subjected to microtensile bond strength tests after 24 h of water storage. The obtained data were statistically analyzed with three-way analysis of variance (ANOVA) and t tests (alpha = 0.05). RESULTS: The three-way ANOVA results revealed the significant influence of resin coating, resin cement, and curing mode. Resin coating and light curing led to higher bond strengths in almost all groups. Resin-coated dentin with Panavia SA Cement Plus exhibited a mean bond strength greater than 35 MPa in both self-curing and dual-curing modes. CONCLUSIONS: In single-visit CAD/CAM resin restorations, resin coating, resin cement selection, and curing mode influenced the bonding performance of self-adhesive resin cements. In addition, resin coating and light curing increased the bond strength of self-adhesive resin cements. Resin coating and light curing are encouraged for predictable bonding performance of dual-cured self-adhesive resin cements in single-visit CAD/CAM resin restorations.