Effects of different bonding systems with various polymerization modes and root canal region on the bond strength of core build-up resin composite.

Purpose The aim of this study was to clarify the effects of different bonding systems (BSs) with various polymerization modes and root canal regions on the bond strength of core build-up resin composite to dentin.Methods Post cavities were prepared in the roots of 54 bovine teeth. Three types of BS with various polymerization modes (light, chemical, and dual-cure) were applied to the walls of the cavities, which were subsequently filled with core build-up resin composite, and stored in 37 degrees C water for 7 days. Each tooth was then sectioned perpendicular to the long axis of the tooth into 9-disk from the coronal to the apical side. Bond strengths were measured on two-thirds of the disks, while dye penetration was examined in the remaining third.Results Statistical analysis revealed significant differences between the bond strengths of BSs with different polymerization modes, indicating chemical-cured BS had higher bond strength than light-cured BS. The chemical-cured BS group showed cohesive failure in both resin composite and dentin regardless of the root canal region, while adhesive failure was observed in the coronal region for dual-cured BS and in the apical region for light-cured BS. Dye penetration was significantly more at the bonding interface at the apical region of the light-cured BS.Conclusions Chemical-cured BS displayed a greater bond strength than light-cured BS. Cohesive failure was observed in both core build-up resin and dentin, indicating that the integration of tooth structure with resin composite was effective for retaining the resin core and sealing the root canal.