Effect of endodontic sealers on push-out bond strength of CAD-CAM or prefabricated fiber glass posts.

This study aimed to evaluate the effect of endodontic sealer (ES) on bond strength (BS) of prefabricated or milled-CAD-CAM (computer-aided design and computer-aided manufacturing) glass-fiber-posts (GFP). Canals of 90 single-rooted teeth were prepared for filling by the single-cone technique with gutta-percha and one of the following ES: AH Plus (epoxy resin), Endofill (zinc-oxide and eugenol), and Bio-C Sealer (calcium-silicate). After post-space preparation, tooth-specimens were equally divided in half according to type of GFP to be used. In the half to receive milled-CAD-CAM posts, tooth specimens were molded with acrylic resin to obtain replicas. These were scanned to enable the laboratory to produce the milled-CAD-CAM GFPs (Fiber CAD Lab, Angelus) by the subtractive technique. The other half of samples received prefabricated GFPs (Exacto, Angelus) (n=15). The GFPs were cemented with dual-cure resin cement (Panavia F2.0, Kuraray). Each root was sectioned into two slices per root region (cervical, middle, apical) that were subjected to the push-out BS test, in a universal testing machine. Failure mode (FM) was classified by scores. The BS data were submitted to generalized linear model analyses, while FM was analyzed using the chi-square test (a=0.05). BS showed no significant difference among the three ES (p > 0.05). BS was significantly higher for prefabricated (mean 10.84 MPa) versus milled-CAD-CAM GFPs (mean 6.94 MPa) (p <0.0001), irrespective of ES. The majority showed mixed failures. It could be concluded that type of ES did not affect BS of GFPs to dentin, and prefabricated-GFPs had higher bond-strength than customized-milled-CAD-CAM GFPs.