Effects of silver diamine fluoride on demineralization protection after a secondary acid challenge.

OBJECTIVE: This investigation describes the effects of 5% sodium fluoride varnish and 38% silver diamine fluoride on demineralization protection of human enamel lesions of three different severities after a secondary acid challenge. STUDY DESIGN: Specimens underwent color and enamel surface microhardness change measurements after demineralization and treatment events. Transverse microradiography was conducted following the secondary demineralization. RESULTS: After treatments, enamel surface microhardness change showed that 24-hour lesions treated with fluoride varnish had less rehardening than 24-hour lesions treated with silver diamine fluoride (p<0.05), whereas 144-hour lesions from both treatment groups showed a beneficial decrease in surface microhardness change that was markedly better in samples treated with silver diamine fluoride (p<0.05). After the secondary demineralization, 24- and 144-hour lesions treated with silver diamine fluoride showed a sustained beneficial decrease in enamel surface microhardness change when compared to fluoride varnish-treated samples of the corresponding lesion severity (p<0.05). Transverse microradiography showed no difference between fluoride varnish- and silver diamine fluoride-treated samples of any corresponding lesion severity, indicating that remineralization in both fluoride varnish- and silver diamine fluoride-treated samples was proportional to each other after a secondary acid challenge. CONCLUSIONS: Using silver diamine fluoride may have comparable benefits to fluoride varnish in mineral loss prevention.